The appearance of A356 aluminium alloy ingots is standard product shape, sand mold, metal mold casting.
A356.2 Executive standard for chemical composition of cast aluminum alloy ingots: ASTM,
Composition:
Si: 6.5-7.5, Mg: 0.30-0.45, Ti < 0.2, Fe < 0.12, Mn < 0.05, Cu < 0.1, Zn < 0.05, Al balance.
Performance of A356 aluminum metal ingot
The average yield strength, fracture strength, elongation and area shrinkage of cast A356 aluminum alloy at room temperature are 216.64MPa, 224MPa, 1.086% and 0.194% respectively. The increase of the crossing plane distance decreases, while the breaking strength first decreases and then increases, and the elongation does not change significantly with the height.
Reduce the impurity of the A356 alloy and improve the mechanical properties (better than the A356 alloy elongation). It has excellent castability and high strength, and its elongation is suitable for thin materials and places where pressure resistance is required.